You know how it is over there....Just in case it gets nuked, and everyones Mail is invaded : )
In response to : best Paf Clone
Wow, I've never seen so much disrespect in regards to ones comments (Dave Stevens) regarding replicating True Paf tones in a topic that is labled appropriately "best paf Clone" let alone the guy getting shot in the back in the same army? Wtf guys ??? I guess noone can state their results and hard work puplicly without s@!tty comments and negative vibes! Here are some scientific and proven terms which may help to clarify what others have not had the experience of learning and are nieve to facts:
Si (silicone)is to increase the resistivity and reduce eddy currents in AC applications. Si gives the best results in resistivity with the least harm and interference to other properties. Here are two: saturation(B) and core loss (related to H and construction details). permeability matters if you are not magnetizing to high field strengths. Fe (iron), any trace impurity will decrease the Bmax and perm. At low levels almost every type of impurity will have an effect (china material, impureitys in mixtures...unless garanteed and tested through vaporizing). Cold working and strain (bending or shaving) will harm the Magnetic properties also. For transfering the magnetic properties, the lower the carbon the better, so 1002 would usually be better than say 1018 (what 99% of makers use : ) for magnetic application. This is scientific and can be proved and seen in Eq curves...Bmax vs concentration curves. Impurities (Inferior steels not of tight tolerences, this is what makes us winders different and unique) in Fe in Bozorth silicon steel. It has a lower saturation flux density than plain low carbon steel. Silicon steel does have advantages if your electromagnet is going to operate and transfer magnetic properties...Tesla would have known this and used this to his advantage- Thats also proven, and he really should get credit because he really was the first one to invent the radio....Look it up
Perhaps befor being too judgemental and critisize one's quest to achieve true replication of vintage tones, you should first know the amount of information and dedication it takes to discover and research these things. Being judgemental in something you have no experience in is nieve. Its such a shame to see other makers discredit another in public in a topic that you really have to have experience in, and clearly you over looked and took as plain, normal, Nieve, eye of the beholder, etc This is blantantly why i very rarely have this address in my browser. Lets respect eachother and eachothers opinions- Not discredit and be arrogant pricks on things you have no knowledge of..
PEACE....
In response to : best Paf Clone
Wow, I've never seen so much disrespect in regards to ones comments (Dave Stevens) regarding replicating True Paf tones in a topic that is labled appropriately "best paf Clone" let alone the guy getting shot in the back in the same army? Wtf guys ??? I guess noone can state their results and hard work puplicly without s@!tty comments and negative vibes! Here are some scientific and proven terms which may help to clarify what others have not had the experience of learning and are nieve to facts:
Si (silicone)is to increase the resistivity and reduce eddy currents in AC applications. Si gives the best results in resistivity with the least harm and interference to other properties. Here are two: saturation(B) and core loss (related to H and construction details). permeability matters if you are not magnetizing to high field strengths. Fe (iron), any trace impurity will decrease the Bmax and perm. At low levels almost every type of impurity will have an effect (china material, impureitys in mixtures...unless garanteed and tested through vaporizing). Cold working and strain (bending or shaving) will harm the Magnetic properties also. For transfering the magnetic properties, the lower the carbon the better, so 1002 would usually be better than say 1018 (what 99% of makers use : ) for magnetic application. This is scientific and can be proved and seen in Eq curves...Bmax vs concentration curves. Impurities (Inferior steels not of tight tolerences, this is what makes us winders different and unique) in Fe in Bozorth silicon steel. It has a lower saturation flux density than plain low carbon steel. Silicon steel does have advantages if your electromagnet is going to operate and transfer magnetic properties...Tesla would have known this and used this to his advantage- Thats also proven, and he really should get credit because he really was the first one to invent the radio....Look it up
Perhaps befor being too judgemental and critisize one's quest to achieve true replication of vintage tones, you should first know the amount of information and dedication it takes to discover and research these things. Being judgemental in something you have no experience in is nieve. Its such a shame to see other makers discredit another in public in a topic that you really have to have experience in, and clearly you over looked and took as plain, normal, Nieve, eye of the beholder, etc This is blantantly why i very rarely have this address in my browser. Lets respect eachother and eachothers opinions- Not discredit and be arrogant pricks on things you have no knowledge of..
PEACE....